1.4864 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron provides premium quality of 1.4864 Plates.

1.4864 Chemical Composition
Carbon; 0.15max
Silicon; 1.0-2.0
Manganese; 2.00max
Nickel; 33.0-37.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 15.0-17.0
Nickel; 0.11max

1.4864 Mechanical Properties
Tensile Strength(Mpa); 550-750
0.2% proof Strength(Mpa); 230
Elongation; 28-30%
Brinell Hardness; 223

1.4876 Plates

Approx Price: Rs 225 / Kilogram 
Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is involved in offering a wide range of 1.4876 Plates.

1.4876 Chemical Composition

  • Carbon; 0.12max
  • Silicon; 1.00max
  • Manganese; 2.00max
  • Nickel; 30.0-34.0
  • Phosphorus; 0.030max
  • Sulfur; 0.015max
  • Chromium; 19.0-23.0
  • Titanium; 0.15-0.60
  • Aluminum; 0.15-0.60


1.4876 Mechanical Properties

  • Tensile Strength(Mpa); 450-680
  • 0.2% proof strength(Mpa); 170
  • Elongation; 28-30%
  • Brinell Hardness; 192

X8CrNiTi18-10 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is the suppliers of high quality X8CrNiTi18-10 Plates.

X8CrNiTi18-10 Chemical Composition
Carbon; 0.1max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 9.0-12.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 17.0-19.0
Titanium; 0.8max

X8CrNiTi18-10 Mechanical Properties
Tensile Strength(Mpa); 500-720
0.2% proof strength(Mpa); 190
Elongation; 40%min
Brinell Hardness; 215

X8CrCoNiMo10-6 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is the suppliers of high quality X8CrCoNiMo10-6 Plates.

X8CrCoNiMo10-6 Chemical Composition
Carbon; 0.05-0.12
Silicon; 0.1-0.8
Manganese; 0.3-1.3
Nickel; 0.2-1.2
Phosphorus; 0.025max
Sulfur; 0.015max
Chromium; 9.8-11.2
Molybdenum; 0.5-1.00
Tungsten; 0.7max
Vanadium; 0.1-0.4
Cobalt; 5.0-7.0
Nitrogen; 0.035max
Niobium; 0.2-0.5
Boron; 0.005-0.015

X8CrCoNiMo10-6 Mechanical Properties
Tensile Strength(Mpa); 1000-1140
0.2% proof strength(Mpa); 850
Elongation; 10%min

1.4913 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are involved in offering a wide range of 1.4913 Plates.

1.4913 Chemical Composition
Carbon; 0.17-0.23
Silicon; 0.5max
Manganese; 0.4-0.9
Nickel; 0.2-0.6
Phosphorus; 0.025max
Sulfur; 0.015max
Chromium; 10.0-11.5
Molybdenum; 0.5-0.8
Vanadium; 0.1-0.3
Nitrogen; 0.05-0.10
Niobium; 0.25-0.55
Aluminum; 0.02max
Boron; 0.0015max

1.4913 Mechanical Properties
Tensile Strength(Mpa); 900-1050
0.2% proof strength(Mpa); 750
Elongation; 12%min
Brinell hardness; 302

X6CrNiMoB17-12-2 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We provide premium quality of X6CrNiMoB17-12-2 Plates.

X6CrNiMoB17-12-2 Chemical Composition
Carbon; 0.04-0.08
Silicon; 1.00max
Manganese; 2.00max
Nickel; 10.0-13.0
Phosphorus; 0.035max
Sulfur; 0.015max
Chromium; 16.5-18.5
Molybdenum; 2.0-2.5
Nitrogen; 0.11max
Boron; 0.0015-0.0050

X6CrNiMoB17-12-2 Mechanical Properties
Tensile Strength(Mpa); 490-690
0.2% proof strength(Mpa); 205
Elongation; 30-35%

1.4923 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, provides premium quality of 1.4923 Plates.

1.4923 Chemical Composition
Carbon; 0.18-0.24
Silicon; 0.5max
Manganese; 0.4-0.9
Nickel; 0.3-0.8
Phosphorus; 0.025max
Sulfur; 0.015max
Chromium; 11.0-12.5
Molybdenum; 0.8-1.2
Vanadium; 0.25-0.35

1.4923 Mechanical Properties
Tensile Strength(Mpa); 800-950
0.2 % proof strength(Mpa); 600
Elongation; 14%min
Brinell hardness; 302

1.4948 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is engaged in manufacturing and supplying an optimal quality range of 1.4948 Plates.

1.4948 Chemical Composition
Carbon; 0.04-0.08
Silicon; 1.00max
Manganese; 2.00max
Nickel; 8.0-11.0
Phosphorus; 0.035max
Sulfur; 0.015max
Chromium; 17.0-19.0
Nitrogen; 0.1max

Mechanical Properties
Tensile Strength(Mpa); 510-740
0.2% proof strength(Mpa); 190-230
Elongation; 30-45%

1.4951 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are Suppliers of high quality of 1.4951 Plates.

1.4951 Chemical Composition
Carbon; 0.04-0.08
Silicon; 0.7max
Manganese; 2.00max
Nickel; 19.0-22.0
Phosphorus; 0.035max
Sulfur; 0.015max
Chromium; 24.0-26.0
Nitrogen; 0.1max

1.4951 Mechanical Properties
Tensile Strength(Mpa); 510-750
0.2% proof strength(Mpa); 200-220
Elongation; 35%min
Brinell Hardnes; 192

X50CrMoV15 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is engaged in manufacturing and supplying an optimal quality range of X50CrMoV15 Plates.

X50CrMoV15 Chemical Composition
Carbon; 0.45-0.55
Silicon; 1.00max
Manganese; 1.00max
Phosphorus; 0.040max
Sulfur; 0.015max
Chromium; 14.0-15.0
Molybdenum; 0.5-0.8
Vanadium; 0.1-0.2

X50CrMoV15 Mechanical Properties
Tensile Strength(Mpa); 850-900
Elongation; 12%min
Brinell Hardness(HB): 280

X10NiCrSiNb35-22 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is involved in offering a wide range of X10NiCrSiNb35-22 Plates.

X10NiCrSiNb35-22 Chemical Composition
Carbon; 0.15max
Silicon; 1.0-2.0
Manganese; 2.00max
Nickel; 33.0-37.0
Phosphorus; 0.030max
Sulfur; 0.015max
Chromium; 20.0-23.0
Nitrogen; 0.11max
Niobium; 1.0-1.5

X10NiCrSiNb35-22 Mechanical Properties
Tensile Strength(Mpa); 500-650
0.2% proof strength(Mpa); 270
Elongation; 40%min
Brinell Hardness; 200

1.4887 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are engaged in manufacturing and supplying an optimal quality range of 1.4887 Plates.

1.4887 Chemical Composition
Carbon; 0.15max
Silicon; 1.0-2.0
Manganese; 2.00max
Nickel; 33.0-37.0
Phosphorus; 0.030max
Sulfur; 0.015max
Chromium; 20.0-23.0
Nitrogen; 0.11max
Niobium; 1.0-1.5

1.4887 Mechanical Properties
Tensile Strength(Mpa); 500-650
0.2% proof strength(Mpa); 270
Elongation; 40%min
Brinell Hardness; 200

1.4911 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, provides premium quality of 1.4911 Plates.

1.4911 Chemical Composition
Carbon; 0.05-0.12
Silicon; 0.1-0.8
Manganese; 0.3-1.3
Nickel; 0.2-1.2
Phosphorus; 0.025max
Sulfur; 0.015max
Chromium; 9.8-11.2
Molybdenum; 0.5-1.0
Tungsten; 0.7max
Vanadium; 0.1-0.4
Cobalt; 5.0-7.0
Nitrogen; 0.035max
Niobium; 0.2-0.5
Boron; 0.005-0.015

1.4911 Mechanical Properties
Tensile Strength(Mpa); 1000-1140
0.2% proof strength(Mpa); 850
Elongation; 10%min

1.4905 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are involved in offering a wide range of 1.4905 Plates.

1.4905 Chemical Composition
Carbon; 0.09-0.13
Silicon; 0.1-0.5
Manganese; 0.3-0.6
Nickel; 0.1-0.4
Phosphorus; 0.020max
Sulfur; 0.01max
Chromium; 8.5-9.5
Molybdenum; 0.9-1.1
Tungsten; 0.9-1.1
Vandium; 0.18-0.25
Nitrogen; 0.05-0.09
Niobium; 0.06-0.10
Aluminum; 0.04max
Boron; 0.0005-0.0050

1.4905 Mechanical Properties
Tensile Strength(Mpa); 620-850
0.2% proof strength(Mpa); 450
Elongation; 19%min

1.4938 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is engaged in manufacturing and supplying an optimal quality range of 1.4938 Plates.

1.4938 Chemical Composition
Carbon; 0.08-0.15
Silicon; 0.5max
Manganese; 0.4-0.9
Nickel; 2.0-3.0
Phosphorus; 0.025max
Sulfur; 0.015max
Chromium; 11.0-12.5
Molybdenum; 1.5-2.0
Vanadium; 0.25-0.40
Nitrogen; 0.02-0.04

1.4938 Mechanical Properties
Tensile Strength(Mpa); 930-1130
0.2% proof strength(Mpa); 760
Elongation; 14%min

X6CrNiTiB18-10 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is involved in offering a wide range of X6CrNiTiB18-10 Plates.

X6CrNiTiB18-10 Chemical Composition
Carbon; 0.04-0.08
Silicon; 1.00max
Manganese; 2.00max
Nickel; 8.0-11.0
Phosphorus; 0.035max
Sulfur; 0.015max
Chromium; 17.0-19.0
Nitrogen; 8.0-11.0

X6CrNiTiB18-10 Mechanical Properties
Tensile Strength(Mpa); 510-740
0.2% proof strength(Mpa); 190-230
Elongation; 30-45%

1.4318 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is the suppliers of high quality 1.4318 Plates.

1.4318 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 6.0-8.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 16.5-18.5
Nitrogen; 0.1-0.2

1.4318 Mechanical Properties
Tensile Strength(Mpa); 630-850
0.2% proof strength(Mpa); 330-350
Elongation; 35-45%

1.4542 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is involved in offering a wide range of 1.4542 Plates.

1.4542 Chemical Composition
Carbon; 0.07max
Silicon; 0.7max
Manganese; 1.5max
Nickel; 3.0-5.0
Phosphorus; 0.040max
Sulfur; 0.015max
Chromium; 15.0-17.0
Molybdenum; 0.6max
Niobium; 0.45max
Copper; 3.0-5.0

1.4542 Mechanical Properties
Tensile Strength(Mpa); 930-1100
0.2% proof strength(Mpa); 720
Elongation; 12-16%
Brinell Hardness; 360

X5CrNiCuNb16-4 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is engaged in manufacturing and supplying an optimal quality range of X5CrNiCuNb16-4 Plates.

X5CrNiCuNb16-4 Chemical Composition
Carbon; 0.07max
Silicon; 0.7max
Manganese; 1.5max
Nickel; 3.0-5.0
Phosphorus; 0.040max
Sulfur; 0.015max
Chromium; 15.0-17.0
Molybdenum; 0.6max
Niobium; 0.45max
Copper; 3.0-5.0

X5CrNiCuNb16-4 Mechanical Properties
Tensile Strength(Mpa); 930-1100
0.2% proof strength(Mpa); 720
Elongation; 12-16%
Brinell Hardness; 360

X6CrNiNb18-10 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5mm
  • Type: Plate

We provide premium quality of X6CrNiNb18-10 Plates.

X6CrNiNb18-10 Chemical Composition
Carbon; 0.08max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 9.0-12.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chroumium; 17.0-19.0
Niobium; 1.00max

X6CrNiNb18-10 Mechanical Properties
Tensile Strength(Mpa); 500-740
0.2% Proof Strength(Mpa); 200-240
Elongation; 210-230

1.4560 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is the suppliers of high quality 1.4560 Plates.

1.4560 Chemical Composition
Carbon; 0.035max
Silicon; 1.00max
Manganese; 1.5-2.0
Nickel; 8.0-9.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 18.0-19.0
Nitrogen; 0.11max
Copper; 1.5-2.0

1.4560 Mechanical Properties
Tensile Strength(Mpa); 450-790
0.2% proof strength(Mpa); 170
Elongation; 45%min
Brinell Hardness(HB); 215

X7CrNiAl17-7 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is involved in offering a wide range of X7CrNiAl17-7 Plates

X7CrNiAl17-7 Chemical Composition
Carbon; 0.09max
Silicon; 0.7max
Manganese; 1.00max
Nickel; 6.5-7.8
Phosphorus; 0.040max
Sulfur; 0.015max
Chromium; 16.0-18.0
Aluminum; 0.7-1.5

X7CrNiAl17-7 Mechanical Properties
Tensile Strength(Mpa); 850-1030
Elongation; 19%min
Brinell Hardness; 255

1.4571 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is engaged in manufacturing and supplying an optimal quality range of 1.4571 Plates.

1.4571 Chemical Composition
Carbon; 0.08max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 10.5-13.5
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 16.5-18.5
Molybdenum; 2.0-2.5
Titanium; 0.7max

1.4571 Mechanical Properties
Tensile Strength(Mpa); 500-700
0.2% proof strength(Mpa); 190-240
Elongation; 30-45%
Brinell Hardness; 210-215

1.4580 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is the suppliers of high quality 1.4580 Plates.

1.4580 Chemical Composition
Carbon; 0.08max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 10.5-13.5
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 16.5-18.5
Molybdenum; 2.0-2.5
Niobium; 1.00max

1.4580 Mechanical Properties
Tensile Strength(Mpa); 510-740
0.2% proof strength(Mpa); 215-220
Elongation; 35-40%

X6CrNiMoNb17-12-2 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are involved in offering a wide range of X6CrNiMoNb17-12-2 Plates.

X6CrNiMoNb17-12-2 Chemical Composition
Carbon; 0.08max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 10.5-13.5
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 16.5-18.5
Molybdenum; 2.0-2.5
Niobium; 1.00max

X6CrNiMoNb17-12-2 Mechanical Properties
Tensile Strength(Mpa); 510-740
0.2% proof strength(Mpa); 215-220
Elongation; 35-40%
Brinell Hardness; 230

X1CrNiMoAlTi12-10-2 Plates

Approx Price: Rs 250 / Kilogram 
Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is involved in offering a wide range of X1CrNiMoAlTi12-10-2 Plates.

X1CrNiMoAlTi12-10-2 Chemical Composition

  • Carbon; 0.015max
  • Silicon; 0.1max
  • Manganese; 0.1max
  • Nickel; 9.2-10.2
  • Phosphorus; 0.010max
  • Sulfur; 0.005max
  • Chromium; 11.5-12.5
  • Molybdenum; 1.85-2.15
  • Nitrogen; 0.02max
  • Titanium; 0.28-0.40
  • Aluminum; 0.8-1.1


X1CrNiMoAlTi12-10-2 Mechanical Properties

  • Tensile Strength(Mpa); 1400
  • 0.2% proof strength(Mpa); 1300
  • Elongation; 9%min
  • Brinell Hardness; 363

1.4655 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is engaged in manufacturing and supplying an optimal quality range of 1.4655 Plates.

1.4655 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 3.5-5.5
Phosphorus; 0.035max
Sulfur; 0.015max
Chromium; 22.0-24.0
Molybdenum; 0.1-0.6
Nickel; 0.05-2.00
Copper; 1.0-3.0

1.4655 Mechanical Properties
Tensile Strength(Mpa); 600-850
0.2% proof strength(Mpa); 400-420
Elongation; 20-25%

 

1.4650 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is the suppliers of high quality 1.4650 Plates.

1.4650 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 9.0-10.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 18.5-20.0
Nitrogen; 0.08max
Copper; 1.00max

1.4650 Mechanical Properties
Tensile Strength(Mpa); 520-720
0.2% proof strength(Mpa); 210
Elongation; 40-45%

X2CrNiCuN23-4 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, manufactures and supply an optimal quality range of X2CrNiCuN23-4 Plates.

X2CrNiCuN23-4 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 3.5-5.5
Phosphorus; 0.035max
Sulfur; 0.015max
Chromium; 22.0-24.0
Molybdenum; 0.1-0.6
Nitrogen; 0.05-2.00
Copper; 1.0-3.0

X2CrNiCuN23-4 Mechanical Properties
Tensile Strength(Mpa); 600-850
0.2% proof strength(Mpa); 400-420
Elongation; 20-25%

1.4713 Plates

Approx Price: Rs 225 / Kilogram 
Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is engaged in manufacturing and supplying an optimal quality range of 1.4713 Plates.

1.4713 Chemical Composition

  • Carbon; 0.12max
  • Silicon; 0.5-1.0
  • Manganese; 1.00max
  • Phosphorus; 0.040max
  • Sulfur; 0.015max
  • Chromium; 6.0-8.0
  • Aluminum; 0.5-1.0


1.4713 Mechanical Properties

  • Tensile Strength(Mpa); 420-620
  • 0.2% proof strength(Mpa); 220
  • Elongation; 15-20%
  • Brinell Hardness; 192

X6CrNiSiNCe19-10 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels provide premium quality X6CrNiSiNCe19-10 Plates.

X6CrNiSiNCe19-10 Chemical Composition
Carbon; 0.04-0.08
Silicon; 1.0-2.0
Manganese; 1.00max
Nickel; 9.0-11.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 18.0-20.0
Cerium; 0.03-0.08
Nitrogen; 0.12-0.20

X6CrNiSiNCe19-10 Mechanical Properties
Tensile Strength(Mpa); 600-800
0.2% proof strength(Mpa); 290
Elongation; 30-40%
Brinell hardness; 210

X25CrMnNiN25-9-7 Sheets

Product Details:
  • Thickness: 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is engaged in manufacturing and supplying an optimal quality range of X25CrMnNiN25-9-7 Sheets.

Chemical Composition
Carbon; 0.2-0.3
Silicon; 1.00max
Manganese; 8.0-10.0
Nickel; 6.0-8.0
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 24.0-26.0
Nitrogen; 0.2-0.4

Mechanical Properties
Tensile Strength(Mpa); 850-1050
0.2% proof strength(Mpa); 500
Elongation; 25%min
Hardness Brinell; 311

X1CrNiMoCuN24-22-8 Sheets

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5mm
  • Surface Treatment: Coated
  • Type: Sheets

Aesteiron Steels Pvt Ltd, is the suppliers of high quality X1CrNiMoCuN24-22-8 Sheets.

Chemical Composition
Carbon; 0.02max
Silicon; 0.5max
Manganese; 2.0-4.0
Nickel; 21.0-23.0
Phosphorus; 0.030max
Sulfur; 0.005max
Chromium; 23.0-25.0
Molybdenum; 7.0-8.0
Nitrogen; 0.45-0.55
Copper; 0.3-0.6

Mechanical Properties
Tensile Strength, Mpa: 750-1000
0.2% proof strength, Mpa: 430
Elongation; 40%min
Brinell hardness; 310

X6CrNiCuS18-9-2 Sheets

Product Details:
  • Material: Stainless Steel
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5mm
  • Type: Sheets

Aesteiron Steels Pvt Ltd, provides premium quality of X6CrNiCuS18-9-2 Sheets.

Chemical Composition
Carbon; 0.08max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 8.0-10.0
Phosphorus; 0.045max
Sulfur; 0.15-0.35
Chromium; 17.0-19.0
Molybdenum; 0.60max
Nitrogen; 0.11max
Copper; 1.4-1.8

Mechanical Properties
Tensile Strength, Mpa: 500-710
0.2% proof strength, Mpa: 185
Elongation; 35%min
Brinell hardness(HB); 215

X3CrNiCu18-9-4 Sheets

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5mm
  • Surface Treatment: Coated, Painted, Hot Rolled, Cold Rolled
  • Type: Sheets

We are involved in offering a wide range of X3CrNiCu18-9-4 Sheets.

Chemical Composition
Carbon; 0.04max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 8.5-10.5
Phosphorus; 0.045max
Sulfur; 0.030max
Chromium; 17.0-19.0
Nitrogen; 0.11max
Copper; 3.0-4.0

 


Mechanical Properties
Tensile Strength, Mpa: 450-740
0.2% proof strength, Mpa: 175
Elongation; 45%min
Brinell Hardness(HB); 215

X1NiCrMoCu31-27-4 Sheets

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, provides premium quality of X1NiCrMoCu31-27-4 Sheets.

Chemical Composition
Carbon; 0.02max
Manganese; 2.00max
Nickel; 30.0-32.0
Phosphorus; 0.030max
Sulfur; 0.010max
Chromium; 26.0-28.0
Molybdenum; 3.0-4.0
Nitrogen; 0.11max
Copper; 0.7-1.5

Mechanical Properties
Tensile Strength(Mpa); 500-750
0.2% Proof Strength(Mpa); 215-250
Elongation; 30-40%

X2NiCrAlTi32-20 Sheets

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are involved in offering a wide range of X2NiCrAlTi32-20 Sheets.

Chemical Composition
Carbon; 0.03max
Silicon; 0.7max
Manganese; 1.00max
Nitrogen; 32.0-35.0
Phosphorus; 0.020max
Sulfur; 0.015max
Chromium; 20.0-23.0
Titanium; 0.6max
Aluminum; 0.15-0.45

Mechanical Properties
Tensile Strength, Mpa: 450-700
0.2% Proof Strength, Mpa: 180
Elongation; 30-35%

X1CrNiMoCuN25-25-5 Sheets

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are engaged in manufacturing and supplying an optimal quality range of X1CrNiMoCuN25-25-5 Sheets.

Chemical Composition
Carbon; 0.02max
Silicon; 0.7max
Manganese; 2.00max
Nickel; 24.0-27.0
Phosphorus; 0.030max
Sulfur; 0.01max
Chromium; 24.0-26.0
Molybdenum; 4.7-5.7
Nitrogen; 0.17-0.25
Copper; 1.0-2.0

Mechanical Properties
Tensile Strength(Mpa); 600-800
0.2% proof strength(Mpa); 290-300
Elongation; 35-40%
Brinell hardness(HB); 250

X3CrNiMo13-4 Sheets

Product Details:
  • Standard: ASTM
  • Surface Treatment: Coated
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron provides premium quality of X3CrNiMo13-4 Sheets.

Chemical Composition
Carbon; 0.05max
Silicon; 0.7max
Manganese; 1.5max
Nickel; 3.5-4.5
Phosphorus; 0.040max
Sulfur; 0.015max
Chromium; 12.0-14.0
Molybdenum; 0.3-0.7
Nitrogen; 0.02max

Mechanical Properties
Tensile Strength(Mpa); 1100
0.2% proof strength(Mpa); 520-800
Elongation; 11-17
Brinell Hardness(HB); 320

1.4313 Sheets

Product Details:
  • Color: Silver
  • Surface Treatment: Coated
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron Steels Pvt Ltd, is engaged in manufacturing and supplying an optimal quality range of 1.4313 Sheets.

Chemical Composition
Carbon; 0.05max
Silicon; 0.7max
Manganese; 1.5max
Nickel; 3.5-4.5
Phosphorus; 0.040max
Sulfur; 0.015max
Chromium; 12.0-14.0
Molybdenum; 0.3-0.7
Nitrogen; 0.02max

Mechanical Properties
Tensile Strength(Mpa); 1100
0.2% proof strength(Mpa); 520-800
Elongation; 11-17%
Brinell Hardness(HB); 320