EN 10088-1Sheet Plate

1.4307 Sheets

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5mm
  • Type: Sheets

Aesteiron provides premium quality of 1.4307 Sheets.

1.4307 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 8.0-10.5
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 17.5-19.5
Nitrogen; 0.11max

1.4307 Mechanical Properties
Tensile Strength(Mpa); 450-700
0.2% proof strength(Mpa); 170-220
Elongation; 35-45%
Brinell Hardness; 200-215

1.4311 Sheets

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5mm
  • Type: Sheets

Aesteiron Steels Pvt Ltd, is involved in offering a wide range of 1.4311 Sheets.

1.4311 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 8.5-11.5
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 17.5-19.5
Nitrogen; 0.12-0.22

1.4311 Mechanical Properties
Tensile Strength(Mpa); 550-760
0.2% Proof Strength(Mpa); 270-305
Elongation; 30-45%
Brinell Hardness; 210-230

X2CrNiN18-10 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5mm
  • Type: Sheets

Aesteiron is engaged in manufacturing and supplying an optimal quality range of X2CrNiN18-10 Plates.

X2CrNiN18-10 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 2.00max
Nickel; 8.5-11.5
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 17.5-19.5
Nitrogen; 0.12-0.22

X2CrNiN18-10 Mechanical Properties
Tensile Strength(Mpa); 550-760
0.2% Proof Strength(Mpa); 270-305
Elongation; 270-305%
Brinell Hardness(HB); 210-230

1.4319 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are involved in offering a wide range of 1.4319 Sheets & Plates.

1.4319 Chemical Composition
Carbon; 0.07max
Silicon; 1.00max
Manganese; 2.00max
Nitrogen; 6.0-8.0
Phosphorus; 0.045max
Sulfur; 0.03max
Chromium; 16.0-18.0
Nitrogen; 0.11max

1.4319 Mechanical Properties
Tensile Strength(Mpa); 500-750
0.2% Proof Strength(Mpa); 190-230
Elongation; 45%min
Brinell Hardness(HB); 215

1.4371 Sheets

Product Details:
  • Tensile Strength: 630-850 Mpa
  • Proof Strength: 280-300 Mpa
  • Elongation: 35-45%
  • Standard: ASTM, AISI
  • Surface Treatment: Coated, Painted, Hot Rolled
  • Steel Grade: SS 304, SS316 L, SS304 L

Aesteiron provides premium quality of 1.4371 Sheets.

Chemical Composition:

  • Carbon- 0.03max
  • Silicon- 1.00max
  • Manganese- 6.0-8.0
  • Nickel- 3.6-5.5
  • Phosphorus- 0.045max
  • Sulphur- 0.015max
  • Chromium- 16.0-17.0
  • Nitrogen- 0.15-0.20

X2CrMnNiN17-7-5 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are suppliers of high quality of X2CrMnNiN17-7-5 Plates.

X2CrMnNiN17-7-5 Chemical Composition
Carbon; 0.03max
Silicon; 1.00max
Manganese; 6.0-8.0
Nickel; 3.6-5.5
Phosphorus; 0.045max
Sulfur; 0.015max
Chromium; 16.0-17.0
Nitrogen; 0.15-0.20

X2CrMnNiN17-7-5 Mechanical Properties
Tensile Strength(Mpa); 630-850
0.2% Proof Strength(Mpa); 280-300
Elongation; 35-45%

1.4373 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

Aesteiron is involved in offering a wide range of 1.4373 Plates.

1.4373 Chemical Composition
Carbon; 0.15max
Silicon; 1.00max
Manganese; 7.5-10.5
Nickel; 4.0-6.0
Phosphorus; 0.045max
Chromium; 17.0-19.0
Nitrogen; 0.5-0.25

1.4373 Mechanical Properties
Tensile Strength(Mpa); 600-880
0.2% Proof Strength(Mpa); 320-340
Elongation; 35-45%

1.4418 Plates

Product Details:
  • Thickness: 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm

We are engaged in manufacturing and supplying an optimal quality range of 1.4418 Plates.

1.4418 Chemical Composition
Carbon; 0.06max
Silicon; 0.7max
Manganese; 1.5max
Nickel; 4.0-6.0
Phosphorus; 0.040max
Sulfur; 0.015max
Chromium; 15.0-17.0
Molybdenum; 0.8-1.5
Nitrogen; 0.02max

1.4418 Mechanical Properties
Tensile Strength(Mpa); 760-1100
0.2% proof strength(Mpa); 550-700
Elongation; 14-16%
Brinell Hardness(HB); 320